Alkaline battery

ABSTRACT

An alkaline battery includes: a negative electrode including a zinc or zinc alloy powder as an active material; an alkaline electrolyte; and a positive electrode. The zinc or zinc alloy powder has a specific surface area of 0.01 to 10 m 2 /g, and the weight ratio of the electrolyte to the negative electrode active material is in the range of 0.1 to 2. This invention can provide an alkaline battery that is improved in electrolyte leakage resistance and high-rate discharge characteristics.

TECHNICAL FIELD

The present invention relates to alkaline batteries using a zinc or zinc alloy powder as a negative electrode active material, and, more particularly, to prevention of gas production and an improvement in high-rate discharge characteristics.

BACKGROUND ART

A conventional problem with alkaline batteries using a zinc or zinc alloy powder as a negative electrode active material is that the active material powder corrodes in an alkaline electrolyte to produce hydrogen gas. Accumulation of this gas in the battery increases the battery inner pressure, thereby causing a problem of electrolyte leakage.

To solve this problem, various techniques have been examined. Japanese Laid-Open Patent Publication No. Hei 8-78017 discloses that regulating the specific surface area of a zinc alloy powder to 0.013 to 0.03 m²/g decreases the reactivity of the active material powder with electrolyte, thereby reducing the amount of gas produced.

Patent Document 1: Japanese Laid-Open Patent Publication No. Hei 8-78017

DISCLOSURE OF INVENTION Problem That the Invention is to Solve

However, the following problems arise. When a zinc or zinc alloy powder serving as an active material has a small specific surface area, i.e., a large particle size, the amount of the active material powder filled in a limited volume is small, thereby resulting in a decrease in capacity. On the other hand, when a zinc or zinc alloy powder has a large specific surface area, the amount of electrolyte per unit surface area of the active material powder is small, thereby resulting in degradation of the high-rate discharge characteristics of the battery. When the amount of electrolyte per unit surface area of the active material powder is insufficient, the concentration of Zn(OH)₄ ²⁻ produced during charge sharply increases at the surface of the active material particles. These ions increase resistance, thereby resulting in a significant degradation of discharge characteristics, particularly high-rate discharge characteristics. Further, the reactivity of the active material with electrolyte becomes excessively high, so that the amount of hydrogen gas production sharply increases.

An object of the present invention is to optimize the balance between the amount of electrolyte per unit surface area of a negative electrode active material and the specific surface area of the negative electrode active material in order to improve the high-rate discharge characteristics of a battery, and to suppress gas production in order to improve the leakage-resistance characteristics of the battery.

MEANS FOR SOLVING THE PROBLEM

In order to solve the problems as described above, the present invention relates to an alkaline battery including: a negative electrode including a negative electrode mixture that contains a zinc or zinc alloy powder as an active material; an alkaline electrolyte; and a positive electrode. The negative electrode active material powder has a specific surface area of 0.01 to 10 m²/g, and the weight ratio of the electrolyte to the negative electrode active material is 0.1 to 2.

It is preferred that the negative electrode mixture contain 0.15 to 0.9 wt % of lithium hydroxide.

EFFECTS OF THE INVENTION

The present invention can optimize the relation between a negative electrode active material powder and electrolyte and provide an alkaline battery that is improved in electrolyte leakage resistance and high-rate discharge characteristics.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a longitudinal sectional view of a cylindrical alkaline dry battery according to an Example of the present invention; and

FIG. 2 is a longitudinal sectional view of an air battery according to an Example of the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

The present invention relates to an alkaline battery including: a negative electrode including a negative electrode mixture that contains a zinc or zinc alloy powder as an active material; an alkaline electrolyte; and a positive electrode. The negative electrode active material powder has a specific surface area of 0.01 to 10 m²/g, and the weight ratio of the electrolyte to the negative electrode active material powder (electrolyte/negative electrode active material) is in the range of 0.1 to 2.

It is preferred that the negative electrode mixture contain 0.15 to 0.9 wt % of lithium hydroxide.

In the alkaline battery of the present invention, the amount of electrolyte per unit surface area of the negative electrode active material powder is optimized. Thus, Zn(OH)₄ ²⁻ around the negative electrode active material powder is diffused, so that Zn(OH)² and ZnO are prevented from depositing on the surface of the negative electrode active material powder. As a result, the discharge characteristics, particularly high-rate discharge characteristics, of the battery improve.

If the weight ratio (electrolyte)/(negative electrode active material) is less than 0.1, the concentration of Zn(OH)₄ ²⁻ around the negative electrode active material powder sharply increases, thereby resulting in degradation of the high-rate discharge characteristics of the battery. Also, if this ratio is greater than 2, the ratio of the electrolyte to the negative electrode mixture increases excessively. As a result, the amount of the active material powder in the negative electrode mixture decreases, thereby resulting in a decrease in battery capacity.

On the other hand, if the specific surface area of the negative electrode active material powder is less than 0.01 m²/g, the size of the active material particles themselves becomes too large, so that the reactivity of the active material with the electrolyte decreases, thereby leading to a decrease in capacity. On the other hand, if the specific surface area of the negative electrode active material powder is greater than 10 m²/g, the reactivity of the active material with the electrolyte becomes too high, thereby promoting the corrosion of the active material powder and increasing the amount of gas produced.

Further, when the negative electrode mixture contains 0.15 to 0.9 wt % of lithium hydroxide, the corrosion of the zinc or zinc alloy powder is suppressed, so that the production of hydrogen gas can be prevented.

As the zinc alloy, a zinc alloy containing at least one selected from the group consisting of Al, Bi, In, and Ca, having high hydrogen overvoltages, is effective for suppressing gas production and preferable. Besides, Sn or Pb is also effective as the element to be added.

Embodiment 1

The structure of an alkaline dry battery is described with reference to FIG. 1, which is a partially sectional front view.

A battery case 1 contains a positive electrode mixture 2 in the form of short cylindrical pellets, a separator 4, and a gelled negative electrode 3. The battery case 1 may be a steel case whose inner face is plated with nickel. A plurality of the positive electrode mixture pellets 2 are contained in the battery case 1 so as to closely adhere to the inner face thereof. The separator 4 is placed on the inner side of the positive electrode mixture 2, and the gelled negative electrode 3 is filled in the space on the inner side of the separator 4.

The positive electrode mixture 2 is prepared as follows. First, manganese dioxide, graphite, and an electrolyte are mixed together in a weight ratio of 90:6:1. The resultant mixture is sufficiently stirred and then compression molded into flakes. Subsequently, the positive electrode mixture flakes are crushed into granules. The positive electrode mixture granules are then classified with a sieve to obtain granules of 10 to 100 mesh. The resultant granules are compression molded into hollow cylinders to obtain the positive electrode mixture pellets 2. Four positive electrode mixture pellets 2 are inserted into the battery case 1, and the positive electrode mixture 2 is again molded in the battery case 1 by means of a compressing device so as to closely adhere to the inner wall of the battery case 1.

The separator 4, which is a cylinder with a bottom, is placed in the middle of the positive electrode mixture 2 that is placed in the battery case 1 in the above manner, and a predetermined amount of an alkaline electrolyte is injected into the space on the inner side of the separator 4. After the lapse of a predetermined time, the gelled negative electrode mixture 3, which comprises the alkaline electrolyte, a gelling agent, and a zinc alloy powder, is filled into the space on the inner side of the separator 4. The gelled negative electrode mixture 3 used is a mixture composed of 1 wt % of sodium polyacrylate serving as the gelling agent, 33 wt % of the alkaline electrolyte, and 66 wt % of the zinc alloy powder. Also, the separator 4 used is a 220-μm-thick non-woven fabric composed of polyvinyl alcohol fibers and rayon fibers in a weight ratio of 7:10. The density of the separator is 0.30 g/cm³, and the size of the separator fibers is 0.3 denier. The ratio of the fibers is not limited to this, and other fibers may be added as a binder.

Subsequently, a negative electrode current collector 6 is inserted into the middle of the gelled negative electrode mixture 3. The negative electrode current collector 6 is integrally combined with a gasket 5 and a bottom plate 7 serving as the negative electrode terminal. The open edge of the battery case 1 is crimped onto the circumference of the bottom plate 7 with the edge of the gasket 5 interposed therebetween, to seal the opening of the battery case 1. Lastly, the outer face of the battery case 1 is covered with an outer label 8.

The electrolyte used is an alkaline electrolyte prepared by dissolving KOH in water. The KOH concentration of the alkaline electrolyte is 30 wt % to 45 wt %. In order to suppress the self-discharge of zinc, ZnO may be dissolved in the electrolyte, and with respect to the dissolution amount, ZnO may be dissolved until it becomes saturated at each alkali concentration. To reduce the production of hydrogen gas, an organic anti-corrosive agent may be dispersed in the electrolyte.

Any organic anti-corrosive agent may be used as long as it suppresses the production of hydrogen, and an example is fluoroalkyl polyoxyethylene (trade name: Surflon #S-161). Also, the electrolyte may be in the state of gel. Any gelling agent may be used if it combines with the alkaline electrolyte to form gel, and examples other than sodium polyacrylate include carboxymethyl cellulose, polyvinyl alcohol, polyethylene oxide, polyacrylic acid, sodium polyacrylate, chitosan gel, and modified materials thereof obtained by changing the polymerization reaction, cross-linking degree, or molecular weight.

Embodiment 2

The structure of an air battery is described with reference to FIG. 2. FIG. 2 is a partially sectional front view of an air battery. FIG. 2 illustrates the structure immediately after the fabrication; due to discharge, zinc in the negative electrode changes to a zinc oxide and undergoes a volume expansion, so that the space in an air diffusion chamber 16 changes to a size that is so large as to accommodate only an air diffusion paper 15.

A case serving as the positive electrode terminal is represented by numeral 11 and contains a separator 12, an air electrode 13 and a water-repellent film 14 on the bottom. Under them is the air diffusion chamber 16 for accommodating the air diffusion paper 15. The water-repellent film 14 allows oxygen to be supplied to the air electrode 13 and prevents an electrolyte from leaking out of the battery. The air diffusion paper 15 permits uniform diffusion of air that is introduced from an air vent 17 in the bottom of the case 11 into the case.

A sealing plate 18 serving as the negative electrode terminal contains a negative electrode mixture 19 comprising zinc or a zinc alloy, and a ring-shaped insulating gasket 20 is fitted to the periphery thereof. The sealing plate is combined with the case 11, and the edge of the case 11 is crimped onto the sealing plate with the insulating gasket 20 therebetween, to seal the power generating element. Seal paper 21 affixed to the outer bottom face of the case closes the air vent 17 when the battery is not used, thereby blocking the entrance of air and preventing battery deterioration due to self-discharge. The air electrode 13 is produced by bonding a catalyst composition mainly composed of a metal oxide such as manganese dioxide, graphite, activated carbon, and a fluorocarbon binder to a current collector net under pressure.

EXAMPLES

Examples of the present invention are described below.

Example 1

AA-type alkaline dry batteries as illustrated in Embodiment 1 and coin-type PR2330 air batteries as illustrated in Embodiment 2 were fabricated and evaluated for their characteristics.

The zinc or zinc alloy powders used were synthesized by atomization and classified. In consideration of gas production, the zinc alloys used were alloys containing at least one selected from the group consisting of Al, Bi, In, and Ca at 50 to 1000 ppm.

The specific surface areas of the zinc or zinc alloy powders were measured by a nitrogen adsorption method using an ASAP2010 analyzer available from Micromeritics Instrument Corporation. Preliminary drying of the powders (deaeration) were performed in a vacuum at 120° C. for 5 hours.

Table 1 shows the specific surface areas of the zinc and zinc alloy powders. TABLE 1 Specific surface area of zinc powder Material Metal added to Zinc (m²/g) A1 None 0.005 A2 None 0.01 A3 None 0.1 A4 None 1 A5 None 5 A6 None 10 A7 None 20 A8 Al 0.005 A9 Al 0.01 A10 Bi 0.1 A11 In 1 A12 Ca 2 A13 Al and Bi 5 A14 Al and In 6 A15 Bi and In 8 A16 Bi and Ca 9 A17 Al, Bi and In 10 A18 Ca, Bi and In 10 A19 Al, Bi, In and Ca 10 A20 Al, Bi, In and Ca 15

Table 2 shows the characteristics of the batteries using the negative electrode active materials as listed in Table 1. The characteristics of the batteries were measured as follows.

The respective batteries were placed in a constant temperature oven at 20° C. and a relative humidity of 60% and discharged at a predetermined current density to obtain discharge capacity C2 (mAh). Also, the theoretical capacity C1 (mAh) was calculated from the weight of Zn of each battery. The proportion P (%) of the discharge capacity C2 to the theoretical capacity C1 was calculated from the following formula (1) to evaluate the high-rate discharge characteristics of each battery. The higher the P value, the better are high-rate discharge characteristics. P(%)=(C2/C1)×100  (1)

For the alkaline dry batteries, P values obtained from a 1 A discharge and battery capacities on a 50 mA discharge are shown. For air batteries, P values obtained from a 160 mA discharge and battery capacities on a 3 mA discharge are shown. TABLE 2 Air battery Alkaline dry battery Electrolyte/ Capacity Capacity (zinc or P (%) on (mAh) on P (%) (mAh) zinc alloy) 160 mA 3 mA on 1 A on 50 mA Material weight ratio discharge discharge discharge discharge A1 0.03 2 665 2 1829 A2 0.04 5 760 6 2090 A3 0.05 8 755 9 2076 A4 0.06 10 799 11 2197 A5 0.07 11 820 12 2255 A6 0.08 12 825 13 2269 A7 0.09 14 410 15 1128 A8 0.05 2 562 2 1546 A9 0.02 2 762 2 2096 A10 0.02 3 756 3 2079 A11 0.03 3 765 3 2104 A12 0.03 4 760 4 2090 A13 0.04 8 778 9 2140 A14 0.04 11 802 12 2206 A15 0.05 12 815 13 2241 A16 0.05 13 820 14 2255 A17 0.06 15 830 16 2283 A18 0.07 15 835 17 2296 A19 0.08 17 840 19 2310 A20 0.09 17 410 19 1128 A1 0.1 23 855 25 2351 A2 0.1 65 860 70 2365 A3 0.2 70 930 76 2558 A4 0.7 70 925 76 2544 A5 1.2 71 820 77 2255 A6 2 71 815 77 2241 A7 2 72 411 78 1130 A8 0.1 25 820 27 2255 A9 0.1 63 845 68 2324 A10 0.2 70 935 76 2571 A11 0.3 70 930 76 2558 A12 0.5 71 925 77 2544 A13 0.7 71 920 77 2530 A14 0.9 71 850 77 2338 A15 1 71 720 77 1980 A16 1.2 71 700 77 1925 A17 1.5 72 650 78 1788 A18 1.8 73 580 79 1595 A19 2 73 550 79 1513 A20 2 73 399 79 1097 A1 2.1 23 266 24 732 A2 2.2 75 344 79 946 A3 2.25 80 320 84 880 A4 2.3 81 342 85 941 A5 2.35 82 302 86 831 A6 2.4 82 288 86 792 A7 2.5 83 164 87 451 A8 2.55 29 225 30 618 A9 2.6 84 385 89 1058 A10 2.9 86 332 90 913 A11 2.1 89 321 93 883 A12 2.2 90 315 95 866 A13 2.25 90 305 95 839 A14 2.3 91 295 96 811 A15 2.35 91 270 96 743 A16 2.4 92 230 97 633 A17 2.5 92 215 97 591 A18 2.55 93 210 98 578 A19 2.6 93 205 98 564 A20 2.9 93 164 98 451

When A1 and A8 are used as the negative electrode active materials, the P values of the air batteries on the 160 mA discharge and the P values of the alkaline dry batteries on the 1 A discharge are as low as 30% or less. This indicates that when the specific surface area of the zinc or zinc alloy is less than 0.01 m²/g, the P values on high rate discharge become low. Also, when A7 and A20 are used as the negative electrode active materials, the battery capacities of the air batteries on the 3 mA discharge are as low as approximately 400 mAh. Also, the battery capacities of the alkaline dry batteries on the 50 mA discharge are as low as approximately 1100 mAh. This indicates that when the specific surface area of the zinc or zinc alloy is greater than 10 m²/g, the discharge capacities become low even on a low current discharge.

From the above, it can be seen that the specific surface area of the zinc or zinc alloy is less than 0.01 m²/g and greater than 10 m²/g, the discharge characteristics are poor.

However, even if the specific surface area of the zinc or zinc alloy powder as the negative electrode active material is in the range of 0.01 to 10 m²/g, good characteristics are not obtained unless the weight ratio (electrolyte)/(negative electrode active material) is appropriate.

That is, if the weight ratio (electrolyte)/(negative electrode active material) is less than 0.1, the P values (%) of the air batteries on the 160 mA discharge and the P values (%) of the alkaline dry batteries on the 1A discharge are as low as 20% or less. Also, if the weight ratio (electrolyte)/(negative electrode active material) is greater than 2, the discharge capacities of the air batteries on the 3 mA discharge are 400 mAh or less and the discharge capacities of the alkaline dry batteries on the 50 mA discharge are as low as approximately 1000 mAh.

This indicates that even if the specific surface area of the zinc or zinc alloy powder as the negative electrode active material is in the range of 0.01 to 10 m²/g, when the weight ratio (electrolyte)/(negative electrode active material) is less than 0.1 and greater than 2, the discharge characteristics are poor. Therefore, when the specific surface area of the negative electrode active material powder is in the range of 0.01 to 10 m²/g and the weight ratio (electrolyte)/(negative electrode active material) is in the range of 0.1 to 2, alkaline batteries such as air batteries and alkaline dry batteries exhibit excellent discharge characteristics.

In the above range, when the specific surface area of the negative electrode active material powder is in the range of 0.1 to 5 m²/g and the weight ratio (electrolyte)/(negative electrode active material) is in the range of 0.2 to 0.7, both high-rate discharge characteristics and high discharge capacities are obtained. That is, with the air batteries, the P values on the 160 mA discharge are 70 or more and the capacities on the 3 mA discharge are greater than 900 mA. Also, with the alkaline dry batteries, the P values on the 1 A discharge are 76 or more and the capacities on the 50 mA discharge are greater than 2500 mA.

In the case of the batteries using zinc alloys containing at least one element selected from the group consisting of Al, Bi, In, and Ca in their negative electrodes, almost no leakage occurred after discharge. This is probably because alloying suppresses the production of hydrogen gas. Further, the addition of Sn and/or Pb is also effective. With respect to the amount of each of these elements added to zinc, if it is in the range of 20 ppm to 5000 ppm, gas production can be effectively prevented. If it is in the range of 50 ppm to 1000 ppm, gas production can be more effectively prevented.

Example 2

Air batteries and alkaline dry batteries were produced by setting the specific surface area of the zinc or zinc alloy powder to 0.01 to 10 m²/g, setting the weight ratio (electrolyte)/(negative electrode active material) to 0.1 to 2, and adding lithium hydroxide to the negative electrode mixture in various ratios. The P values (%) and battery capacities (mAh) of these batteries were measured under the same conditions as those of Example 1. Table 3 shows the results. TABLE 3 Electrolyte/ Content of Air battery Alkaline dry battery (zinc or zinc lithium P (%) on Capacity (mAh) Capacity (mAh) alloy) weight hydroxide 160 mA on 3 mA P (%) on on 50 mA Material ratio (wt %) discharge discharge 1 A discharge discharge A3 0.31 0.1 70 920 74 2576 A3 0.31 0.15 85 921 89 2579 A3 0.31 0.2 87 923 91 2584 A3 0.31 0.4 88 925 92 2590 A3 0.31 0.6 89 922 93 2582 A3 0.31 0.7 90 920 95 2576 A3 0.31 0.9 91 919 96 2573 A3 0.31 1 91 780 96 2184 A17 0.34 0.1 72 900 76 2520 A17 0.34 0.15 87 902 91 2526 A17 0.34 0.2 90 905 95 2534 A17 0.34 0.4 91 906 96 2537 A17 0.34 0.6 92 910 97 2548 A17 0.34 0.7 93 905 98 2534 A17 0.34 0.9 93 908 98 2542 A17 0.34 1 94 690 99 1932

When the amount of lithium hydroxide contained in the negative electrode mixture is less than 0.15 wt %, the P values of the air batteries and alkaline dry batteries are in the 70% range. When the amount of lithium hydroxide is greater than 0.9 wt %, the discharge capacities of the air batteries and alkaline dry batteries were not more than 800 mAh and not more than 2200 mAh, respectively.

When the amount of lithium hydroxide contained in the negative electrode mixture is in the range of 0.15 to 0.9 wt %, the P values of the air batteries and alkaline dry batteries were good, specifically 85% or more, and the discharge capacities of the air batteries and alkaline dry batteries were good, specifically not less than 900 mAh and not less than 2500 mAh, respectively.

Also, the effects obtained by the addition of Al and the like to the zinc of the negative electrode were essentially the same as those in Example 1.

INDUSTRIAL APPLICABILITY

The present invention is useful for alkaline batteries, such as air batteries and alkaline dry batteries, that use zinc or a zinc alloy as a negative electrode active material. 

1. An alkaline battery comprising: a negative electrode including an electrode mixture that contains a zinc or zinc alloy powder as an active material; an alkaline electrolyte; and a positive electrode, wherein said zinc or zinc alloy powder has a specific surface area of 0.01 to 10 m²/g, and the weight ratio of said electrolyte to the active material (electrolyte/negative electrode active material) is in the range of 0.1 to
 2. 2. The alkaline battery in accordance with claim 1, wherein said electrode mixture contains 0.15 to 0.9 wt % of lithium hydroxide.
 3. The alkaline battery in accordance with claim 1, wherein said zinc or zinc alloy powder has a specific surface area of 0.1 to 5 m²/g, and the weight ratio of said electrolyte to the active material is in the range of 0.2 to 0.7. 